• To produce pumpable concrete
• To produce high strength, high grade concrete by substantial reduction in water resulting in low permeability and high early strength.
• To produce high workability concrete requiring little or no vibration during placing.

• Improved workability Easier, quicker placing and compaction.
• Increased strength Provides high early
• strength for precast concrete if water reduction is taken advantage of.
• Improved quality Denser, close textured concrete with reduced porosity and hence more durable.
• Higher cohesion Risk of segregation and bleeding minimised; thus aids pumping of concrete
• Chloride free Safe in prestressed concrete and with sulphate resisting cements and marine aggregates

• Conplast SP500 is based on Sulphonated Napthalene
• Polymers and is supplied as a brown liquid instantly dispersible in water.
• Conplast SP500 has been specially formulated to give high water reductions up to 25% without loss of workability or to produce high quality concrete of reduced permeability.

• Trials need to be carried out at site to determine the exact dosage of the admixture for the particular mix design and materials.
• However for normal grades of concrete a dosage from 0.5% - 1.0% by weight of cement is recommended, the dosage may be increased to 1.5% to achieve specific slump
• requirements.
• For microsilica concrete where a high amount of water reduction and slump retention are required, trials need to be carried out to arrive at the correct dosage, as the dosage may increase up to 2.0% or even up to 2.5% by weight of cement depending on mix design and performance required.

• Dosages outside the typical ranges quoted above can be used to meet particular requirements. Contact Fosroc for advice.

• An overdose of above the recommended level of admixture may result in high workability, slight increase in air entrainment and retardation of setting time.
• The ultimate strength of the concrete will not be adversely affected and will generally be higher than for normal concrete if properly placed and cured.

Additional Information:

• Delivery Time: 1-10 days depends upon availibility

• To minimise permeability and increase the waterproofing properties of concrete and cement sand mortars for critical applications like roof slabs and screeds, basements, external plastering, bathroom floors, water tanks, sump, drains etc.

• Liquid admixture: Instant and complete dispersion throughout the mix. Uniform waterproofing throughout concrete matrix.
• High efficiency: Dramatic reduction in permeability of concrete/ mortar
• Improved workability: Improves compaction of concrete and mortar, even where harsh sands or aggregates are used.
• Improved concrete quality: Minimises porosity and honey combing.
• Produces dense homogenous concrete.

• Conplast WL is a dark brown liquid based on lignosulphonates which mixes readily with water and
• therefore disperses evenly.
• Conplast WL waterproof by improving the quality of the concrete or mortar.
• It reduces the water demand for required workability and minimises segregation and bleeding.
• Thus it is more efficient compared to traditional powder waterproofer as its use results in two-fold improvement of concrete or mortar.

• Fosroc provides a technical advisory service for onsite assistance and advice on admixture selection, evaluation trials and dispensing equipment.
• Technical data and guidance can be provided for admixtures and other products for use with fresh and hardened concrete

• Conplast WL is ideal for use with all sand/cement mortars where it is required to reduce permeability to a minimum.

• Conplast WL is recommended for all general mass concrete work where, due to harsh aggregates, difficulty of compaction or mix control, the risk of porosity and permeability
• must be minimised. Eg. Basements, bund walls, tanks, balcony, floor and roof slabs.
• N.B.: The minimum dosage is 125ml and the maximum is 200ml per 50kgs of cement. If maximum dosage is used a minimum of 15% water should be reduced to ensure no loss
• in strength.
• Site trials shall be carried out to arrive at the optimum dosage.
• The required quantity of Conplast WL is measured and stir into the first or second bucket of water.
• Conplast WL water mixture shall be added to the concrete or
• mortar and mixed thoroughly.
• Mixing shall be continued and further water shall be added until the required workability is obtained

• The Fosroc range of associated products includes high strength cementation, epoxy grout, polyester resin based mortar for rapid presenting of steel shims to level or for direct bedding of small base plates; Resin Anchoring systems for same day anchoring of bolts in drilled holes in concrete or rock.
• Also available a range of products for use in construction; viz., admixtures, curing compounds, release agents, flooring systems and repair mortars.

Additional Information:

• Delivery Time: 1-10 days as per availiblity
• Packaging Details: Auramix 400 is available in 200kg and 250kg drums

• To provide excellent acceleration of strength gain at early ages and major increases in strength at all ages by significantly reducing water demand in a concrete mix.
• Particularly suitable for precast concrete and other high early strength requirements.
• To significantly improve the workability of site mixed and precast concrete without increasing water demand.
• To provide improved durability by increasing ultimate strengths and reducing concrete permeability.
• In screeds it reduces the water content required to give suitable workability for placing and compaction

• Major increases in strength at early ages without increased cement contents are of particular benefit in precast concrete, allowing earlier stripping times.
• Makes possible major reductions in water:cement ratio which allow the production of high strength concrete without excessive cement contents.
• Use in production of flowing concrete permits easier construction with quicker placing and compaction and reduced labour costs without increasing water content.
• Increased workability levels are maintained for longer than with ordinary sulphonated melamine admixtures.

• Conplast SP430 is a chloride free, superplasticising admixture based on selected sulphonated napthalene polymers.
• It is supplied as a brown solution which instantly disperses in water.
• Conplast SP430 disperses the fine particles in the concrete mix, enabling the water content of the concrete to perform more effectively.
• The very high levels of water reduction possible allow major increases in strength to be obtained.

• Fosroc provides a technical advisory service for on-site assistance and advice on admixture selection, evaluation trials and dispensing equipment.
• Technical data and guidance can be provided for admixtures and other products for use with fresh and hardened concrete.

• The optimum dosage of Conplast SP430 to meet specific requirements should always be determined by trials using the materials and conditions that will be experienced in use.
• This allows the optimisation of admixture dosage and mix design and provides a
• complete assessment of the concrete mix. Starting points for such trials, based on the primary use of the product, are to use a dosage within the normal typical ranges.
• For high strength, water reduced concrete the normal dosage range is from 0.70 to 2.00 litres/100 kg of cementitious material, including PFA, GGBFS and microsilica.
• For high workability concrete the normal dosage range is from 0.70 to 1.30 litres/100 kg of cementitious material.
• Where a combination of performance is required, such as some increase in workability combined with a reduced water content, then the whole range of dosages from 0.70 to
• 2.00 litres/100 kg of cementitious material can be considered

Additional Information:

• Delivery Time: 1-10 days as per availiblity
• Packaging Details: conplast sp 430 is supplied in 5 , 20 , 200 litre & 250kg drums.